网络 无机胶粘剂; 无机粘结剂; 无机粘合剂
双语例句
- Experimental Study on Fire Resistant Property of Concrete Beams Reinforced by Pasting CFRP Sheet with Inorganic Adhesive
用无机胶粘贴CFRP布加固混凝土梁抗火性能试验研究 - Experimental research on alkali-activated slag high temperature resistant inorganic adhesive pasting CFRP sheets on surface of concrete
用碱激发矿渣耐高温无机胶在混凝土表面粘贴碳纤维布试验研究 - Preparation and application of the silicate inorganic adhesive
硅酸盐无机胶粘剂的研制及应用 - Study of Silicate Inorganic Adhesive
硅酸盐无机胶粘剂的研究 - Reserch on the Relationship between Silicate Inorganic Adhesive And Glue Soil Compressive Strength
硅酸盐无机胶粘剂与胶结土壤抗压强度关系的研究 - Discussion on the Gluing Mechanism of Inorganic Adhesive YW-1
YW&1无机胶粘接机理的探讨 - Ways to Improve the Waterproof of Silicate Inorganic Adhesive
提高硅酸盐无机胶耐水性能的途径 - A Study on Modified Cupric Oxide-Phosphoric Acid Inorganic Adhesive
改性氧化铜&磷酸无机胶粘剂的研究 - Study and Application of the High Temperature and Fused Salt Corrosion Proof Inorganic Adhesive, a Special-purpose Adhesive for Salt-bath Furnace
耐高温耐熔盐腐蚀无机胶&盐浴炉专用胶的研究与应用 - This paper inquired into deeply the reason for being high strength in the puffing-inside adhesion of YW 1 inorganic adhesive from the Chemical, physical and mechanical.
本文从化学、物理、机械三方面深入地探讨了YW-1无机胶套接粘接形成高强度的原因。 - Test Study on Shear Strength of Polycrystalline Diamond Bonded with Copper Oxide Inorganic Adhesive
氧化铜无机胶粘接聚晶金刚石时压剪强度的试验研究 - Application of inorganic adhesive technology in the structure of dies
无机粘接技术在模具结构上的应用 - The compression shear strength of dowel joint of YW-1 inorganic adhesive is 140-180 MPa.
YW-1无机胶用于套接粘接，套接压剪强度可达140-180MPa。 - Structural Composite Board Made from Plant Fiber with Inorganic Adhesive
无机胶粘剂植物纤维建筑复合板材 - Study on the Impermeability of Inorganic Adhesive Soil
无机胶粘岩土的抗渗性能研究 - Study on the Preparation Technics of Copper Oxide-Phosphate Inorganic Adhesive
氧化铜-磷酸盐无机胶粘剂的制备工艺研究 - Relation Between the Nature and Structure of Copper Oxide and the Adhesive Strength of Phosphate Inorganic Adhesive
氧化铜的结构和性质及其与磷酸盐无机粘接剂粘接强度的关系 - The effect of third component on CuO-H_3PO_4 inorganic adhesive has been studied. Experimental results showed that the bonding strength can be increased sharply up to 3.4-fold. Passivation of CuO at high temperature has also been studied.
本文研究了第三组份对CuO&H3PO4无机胶粘剂的影响，试验结果表明：粘接强度可大幅度增加，最高可增加2.4倍。 - Application of inorganic adhesive in concrete repairing work
无机粘结胶在混凝土修补工程中的应用 - The paper designed a formula of silicate inorganic adhesive with the water glass as material. The industry water treating medicine can be adhered to carrying agent of bores-ceramic use the adhesive.
以水玻璃为基料设计了一种无机胶粘剂的配方，制备的硅酸盐胶粘剂可粘接粉粒状工业水处理剂于多孔陶瓷载体上。 - The special-purpose adhesive for salt-bath furnace is a high temperature and fused salt corrosion proof inorganic adhesive prepared by taking acid aluminum phosphate as the base stock and kaolinite as filler components.
盐浴炉专用胶是以酸式磷酸铝为基料、以掺杂高岭石为填料等成分配制成的耐高温耐熔盐腐蚀无机胶。 - Investigation on Torsional Sheath Strength of Dowel Joint of Copper Phosphate A Study on Modified Cupric Oxide-Phosphoric Acid Inorganic Adhesive
磷酸氧化铜无机胶套接扭剪强度研究 - Inorganic adhesive H3PO4 CuO is presented for replacing phenol aldehyde resin adhesive in preparing diamond grinder.
采用无机粘结剂H3PO4CuO取代酚醛树脂粘结剂，制作树脂磨具。 - Inorganic adhesive matrix: geopolymer for fiber fabrics strengthening of concrete structures
用于纤维片材加固混凝土结构的无机粘结材料&地聚物 - Our study group has successfully developed an inorganic adhesive, alkali activated slag cement ( AASCM), with fire resistance duration of at least 600 ℃. Under normal temperature, mechanical properties of the AASCM are superior to that of epoxy resin adhesive.
我所在的课题组成功研制出耐火极限不低于600℃的碱激发矿渣无机胶凝材料（以下简称碱矿渣胶凝材料），这种无机胶凝材料在常温下的力学性能不低于环氧类有机胶。 - Taking inorganic high temperature resistant adhesive as basic material, the heat treatment mechanism of inorganic heat insulation paint was laid down on the basis of the thermostability of inorganic adhesion and paint.
以无机耐高温胶为胶粘剂，分析无机耐高温胶粘剂及无机隔热涂料的热力学稳定性，制定涂料产品固化的热处理机制。 - Bond forming tests including organic binder, calcium, inorganic adhesive series pilot; preparation of composite adhesive for bonding test; use coking coal and organic binder mixed with coke test.
粘接成型试验包括对有机粘接剂、钙系列的无机粘接剂进行试验；配制复合粘接剂进行粘接试验；选用主焦煤与有机粘接剂混合用型焦试验。